| Quantity: | |
|---|---|
Silicon Carbide | Unit | |
Density | ≥g/cm³ | 2.6-3.15 |
Hardness | ≥HV | 9.2-9.6 |
Resistance To Bending Degrees | ≥Mpa | 15.5 |
Fracture Toughness | Mpa.m0.5 | 6-8 |
Maximum Service Temperature | ℃ | ≥1550 |
Coefficient Of Linear Expansion | X10-6 /℃.K | 4.5-11.2 |
Dielectric Constant | 20℃,1MHZ | 26-33 |
Elasticity Modulus | Gpa | 300-330 |
Heat Conductivity Coefficient | W/m.K(20℃) | 45 |